Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Thickness | 76.2 microns | 3.00 mil | Side 1 | ||
102 microns | 4.00 mil | Side 2 | |||
203 microns | 8.00 mil | Substrate | |||
381 microns | 15.0 mil | Overall Thickness | |||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 58 | 58 | Silicone Property | ||
Tensile Strength | 6.21 MPa | 900 psi | Silicone Property | ||
Elongation at Break | 350 % | 350 % | Silicone Property | ||
Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength, side 2 to side 2 | ||
Electrical Properties | Metric | English | Comments | ||
Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
Flammability Test | 3.0 | 3.0 | Inches; Char Length; FTMS 191A; Method 5903 | ||
25 | 25 | Seconds; Flame and Glow Time; FTMS 191A; Method 5903 | |||
Processing Properties | Metric | English | Comments | ||
Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
Descriptive Properties | |||||
Color | White | ||||
Total Product Weight (oz/yd2) | 16.8 | ||||
Uncoated Fabric Break Strength (lb/in) | 200 | Fill direction | |||
250 | Warp direction |