- 密度 [g/cm3]: 1.27
- 拉伸强度 [MPa]: 34.09
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| 2.70 g/cc | 0.0975 lb/in³ | Alloy 1100 Property (Annealed) | |||
| Thickness | 102 microns | 4.00 mil | Laminated Aluminum Foil; Arlon SQA-TMS-003 | ||
| 305 microns | 12.0 mil | Side 1; Arlon SQA-TMS-003 | |||
| 660 microns | 26.0 mil | Overall Thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 10.21 MPa | 1481 psi | Silicone Property; Arlon SQA-TMS-008 | ||
| 87.874 MPa | 12745 psi | Alloy 1100 Property (Annealed); ASTM E345 | |||
| Tensile Strength, Yield | 34.09 MPa | 4945 psi | Alloy 1100 Property (Annealed); ASTM E345 | ||
| Elongation at Break | 263 % | 263 % | Silicone Property; Arlon SQA-TMS-008 | ||
| Peel Strength | 1.77 kN/m | 10.1 pli | Silicone Compound Property - Adhesion Strength to Aluminum; Arlon SQA-TMS-011 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 100 - 300 °C @Pressure 0.000 - 10.0 MPa | 212 - 572 °F @Pressure 0.000 - 1450 psi | |||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 12.0 Month @Temperature 21.1 °C | 12.0 Month @Temperature 70.0 °F | |||
| Component Elements Properties | Metric | English | Comments | ||
| Aluminum, Al | >= 99 % | >= 99 % | Alloy 1100 Property (Annealed) | ||
| Descriptive Properties | |||||
| Rigidity (grams) | 3500 | Arlon Gurley Test; Alloy 1100 Property (Annealed) | |||
| Total Product Weight (oz/yd2) | 19.5 | Arlon SQA-TMS-025 | |||