- 密度 [g/cm3]: 1.62
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 165 microns | 6.50 mil | Side 1; Arlon SQA-TMS-003 | ||
| 178 microns | 7.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 406 microns | 16.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 749 microns | 29.5 mil | Overall Thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 74 | 74 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 5.78 MPa | 838 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 128 % | 128 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 15.6 kN/m | 89.0 pli | Die B; Silicone Property; ASTM D624 | ||
| Peel Strength | 0.719 kN/m | 4.10 pli | Bond Strength (S2 to S2); Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 17.4 kV/mm | 441 kV/in | Arlon SQA-TMS-020 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | V-0 | V-0 | designed to meet | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| 4.98 min @Pressure 0.345 MPa, Temperature 121 °C | 0.0830 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | |||
| Descriptive Properties | |||||
| Color | Brown | ||||
| Total Product Weight (oz/yd2) | 34.8 | Arlon SQA-TMS-025 | |||