- 密度 [g/cm3]: 1.24
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | Side 2 Silicone Property; Arlon SQA-TMS-024 | ||
| 1.35 g/cc | 0.0488 lb/in³ | Side 1 Silicone Property; Arlon SQA-TMS-024 | |||
| Thickness | 102 microns | 4.00 mil | Side 1; Arlon SQA-TMS-003 | ||
| 457 microns | 18.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 965 microns | 38.0 mil | Side 2; Arlon SQA-TMS-003 | |||
| 1520 microns | 60.0 mil | Overall Thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 44 | 44 | Side 2 Silicone Property; ASTM D2240 | ||
| 52 | 52 | Side 1 Silicone Property; ASTM D2240 | |||
| Tensile Strength | 6.14 MPa | 890 psi | Side 1 Silicone Property; ASTM D412 | ||
| 7.58 MPa | 1100 psi | Side 2 Silicone Property; ASTM D412 | |||
| Elongation at Break | 550 % | 550 % | Side 1 Silicone Property; ASTM D412 | ||
| 650 % | 650 % | Side 2 Silicone Property; ASTM D412 | |||
| Peel Strength | 5.47 kN/m | 31.2 pli | Bond Strength; Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 25.1 kV/mm | 638 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 240 min @Temperature 204 °C | 4.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 60.1 | Arlon SQA-TMS-025 | |||