- 弯曲强度 [MPa]: 4.14
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | |||
| Brookfield Viscosity | 10000 cP | 10000 cP | Catalyst | ||
| 3.10e+6 cP | 3.10e+6 cP | Mixed | |||
| 7.00e+6 cP @Temperature 25.0 °C | 7.00e+6 cP @Temperature 77.0 °F | Compound | |||
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 20 - 25 | 20 - 25 | |||
| Tensile Strength, Ultimate | 4.14 MPa | 600 psi | |||
| Elongation at Break | 500 % | 500 % | |||
| Tear Strength | 21.0 kN/m | 120 pli | |||
| Thermal Properties | Metric | English | Comments | ||
| Heat Distortion Temperature | 232 °C | 450 °F | estimate | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 480 min @Temperature 24.0 °C | 8.00 hour @Temperature 75.2 °F | handling time | ||
| 1440 min @Temperature 24.0 °C | 24.0 hour @Temperature 75.2 °F | 90% cure | |||
| 2880 min @Temperature 24.0 °C | 48.0 hour @Temperature 75.2 °F | full cure | |||
| Pot Life | 60 min @Temperature 25.0 °C | 60 min @Temperature 77.0 °F | |||
| Shelf Life | 6.00 Month | 6.00 Month | |||
| Descriptive Properties | |||||
| Mix Ratio | 10:1 by weight | ||||