- 弯曲强度 [MPa]: 5.52
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | |||
| Brookfield Viscosity | 10000 cP | 10000 cP | Mixed | ||
| 140000 cP @Temperature 25.0 °C | 140000 cP @Temperature 77.0 °F | Compound | |||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | |||
| Tensile Strength, Ultimate | 5.52 MPa | 800 psi | |||
| Elongation at Break | 200 % | 200 % | |||
| Tear Strength | 15.8 kN/m | 90.0 pli | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -59.4 °C | -75.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 60.0 °C | 0.250 hour @Temperature 140 °F | 10% cure | ||
| 24.0 min @Temperature 60.0 °C | 0.400 hour @Temperature 140 °F | 90% cure | |||
| Pot Life | 120 min @Temperature 25.0 °C | 120 min @Temperature 77.0 °F | |||
| Shelf Life | 6.00 Month | 6.00 Month | |||
| Descriptive Properties | |||||
| Mix Ratio | 10:1 by weight | ||||