- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.04
- 缺口冲击强度: 0.27
- 断裂伸长率 [%]: 140
- 弯曲强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 13.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 - 1.90 g/cc | 0.0614 - 0.0686 lb/in³ | Average value: 1.78 g/cc Grade Count:6 |
| Water Absorption | 0.0400 - 0.350 % | 0.0400 - 0.350 % | Average value: 0.170 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00150 - 0.00300 cm/cm | 0.00150 - 0.00300 in/in | Average value: 0.00213 cm/cm Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 80.0 - 90.0 | 80.0 - 90.0 | Average value: 85.0 Grade Count:4 |
| Tensile Strength, Ultimate | 50.0 - 125 MPa | 7250 - 18100 psi | Average value: 90.5 MPa Grade Count:6 |
| Flexural Yield Strength | 140 - 240 MPa | 20300 - 34800 psi | Average value: 182 MPa Grade Count:6 |
| Flexural Modulus | 13.8 - 17.0 GPa | 2000 - 2470 ksi | Average value: 15.2 GPa Grade Count:6 |
| Compressive Yield Strength | 234 - 275 MPa | 33900 - 39900 psi | Average value: 249 MPa Grade Count:6 |
| Izod Impact, Notched | 0.270 - 0.590 J/cm | 0.506 - 1.11 ft-lb/in | Average value: 0.413 J/cm Grade Count:3 |
| Charpy Impact, Notched | 0.340 - 0.500 J/cm² | 1.62 - 2.38 ft-lb/in² | Average value: 0.413 J/cm² Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 11.4 - 32.0 kV/mm | 290 - 813 kV/in | Average value: 16.1 kV/mm Grade Count:5 |
| Arc Resistance | 135 - 180 sec | 135 - 180 sec | Average value: 164 sec Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 5.00 - 25.0 µm/m-°C | 2.78 - 13.9 µin/in-°F | Average value: 15.0 µm/m-°C Grade Count:6 |
| Thermal Conductivity | 0.410 - 0.790 W/m-K | 2.85 - 5.48 BTU-in/hr-ft²-°F | Average value: 0.583 W/m-K Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 155 - 282 °C | 311 - 540 °F | Average value: 258 °C Grade Count:6 |