- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 0.03
- 缺口冲击强度: 0.163
- 断裂伸长率 [%]: 60.0
- 弯曲强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 7.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 - 2.10 g/cc | 0.0560 - 0.0759 lb/in³ | Average value: 1.87 g/cc Grade Count:23 |
| Water Absorption | 0.0300 - 0.150 % | 0.0300 - 0.150 % | Average value: 0.0842 % Grade Count:16 |
| Linear Mold Shrinkage | 0.000600 - 0.00350 cm/cm | 0.000600 - 0.00350 in/in | Average value: 0.00197 cm/cm Grade Count:23 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 80.0 - 125 | 80.0 - 125 | Average value: 97.9 Grade Count:13 |
| Tensile Strength, Ultimate | 31.0 - 108 MPa | 4500 - 15700 psi | Average value: 74.4 MPa Grade Count:23 |
| Elongation at Break | 0.272 - 1.80 % | 0.272 - 1.80 % | Average value: 0.708 % Grade Count:19 |
| Modulus of Elasticity | 9.50 - 30.0 GPa | 1380 - 4350 ksi | Average value: 18.7 GPa Grade Count:19 |
| Flexural Yield Strength | 60.0 - 190 MPa | 8700 - 27600 psi | Average value: 137 MPa Grade Count:23 |
| Flexural Modulus | 7.50 - 27.0 GPa | 1090 - 3920 ksi | Average value: 16.7 GPa Grade Count:23 |
| Compressive Yield Strength | 156 - 410 MPa | 22600 - 59500 psi | Average value: 250 MPa Grade Count:23 |
| Poissons Ratio | 0.310 - 0.330 | 0.310 - 0.330 | Average value: 0.317 Grade Count:3 |
| Shear Modulus | 5.46 - 5.98 GPa | 792 - 867 ksi | Average value: 5.76 GPa Grade Count:3 |
| Izod Impact, Notched | 0.163 - 0.450 J/cm | 0.305 - 0.843 ft-lb/in | Average value: 0.363 J/cm Grade Count:12 |
| Charpy Impact Unnotched | 0.400 - 1.50 J/cm² | 1.90 - 7.14 ft-lb/in² | Average value: 0.928 J/cm² Grade Count:10 |
| Charpy Impact, Notched | 0.195 - 0.550 J/cm² | 0.928 - 2.62 ft-lb/in² | Average value: 0.341 J/cm² Grade Count:20 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.90e+11 - 1.74e+15 ohm-cm | 1.90e+11 - 1.74e+15 ohm-cm | Average value: 1.77e+14 ohm-cm Grade Count:10 |
| Insulation Resistance | 1.00e+11 - 1.00e+14 ohm | 1.00e+11 - 1.00e+14 ohm | Average value: 2.19e+13 ohm Grade Count:3 |
| Dielectric Constant | 4.50 - 5.60 | 4.50 - 5.60 | Average value: 5.13 Grade Count:11 |
| Dielectric Strength | 8.60 - 35.0 kV/mm | 218 - 889 kV/in | Average value: 17.7 kV/mm Grade Count:20 |
| Dissipation Factor | 0.0120 - 0.286 | 0.0120 - 0.286 | Average value: 0.0557 Grade Count:11 |
| Arc Resistance | 48.0 - 185 sec | 48.0 - 185 sec | Average value: 152 sec Grade Count:13 |
| Comparative Tracking Index | 175 - 325 V | 175 - 325 V | Average value: 207 V Grade Count:17 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.0 - 30.0 µm/m-°C | 6.67 - 16.7 µin/in-°F | Average value: 18.4 µm/m-°C Grade Count:14 |
| 49.0 - 75.0 µm/m-°C @Temperature 40.0 - 130 °C | 27.2 - 41.7 µin/in-°F @Temperature 104 - 266 °F | Average value: 62.0 µm/m-°C Grade Count:2 | |
| CTE, linear, Transverse to Flow | 20.0 - 45.0 µm/m-°C | 11.1 - 25.0 µin/in-°F | Average value: 28.7 µm/m-°C Grade Count:10 |
| Thermal Conductivity | 0.580 - 0.580 W/m-K @Temperature 100 - 100 °C | 4.03 - 4.03 BTU-in/hr-ft²-°F @Temperature 212 - 212 °F | Average value: 0.580 W/m-K Grade Count:1 |
| Maximum Service Temperature, Air | 150 - 250 °C | 302 - 482 °F | Average value: 211 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 - 282 °C | 338 - 540 °F | Average value: 229 °C Grade Count:23 |
| Deflection Temperature at 8.0 MPa | 150 - 185 °C | 302 - 365 °F | Average value: 166 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:19 |
| Shrinkage | 0.000600 - 0.200 % | 0.000600 - 0.200 % | Average value: 0.0684 % Grade Count:19 |