- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.6
- 缺口冲击强度: 1.55
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 - 1.46 g/cc | 0.0499 - 0.0527 lb/in³ | Molding; IS 867-1963 |
| Water Absorption | 0.60 - 1.0 % | 0.60 - 1.0 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0032 - 0.0049 cm/cm | 0.0032 - 0.0049 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | >= 35.0 MPa | >= 5080 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | >= 56.0 MPa | >= 8120 psi | 2mm/min.; IS 867-1963 |
| Izod Impact, Notched | >= 1.55 J/cm | >= 2.90 ft-lb/in | IS 13411-1992 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 0.333 - 0.500 min | 0.00556 - 0.00833 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | |