- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 - 1.82 g/cc | 0.0614 - 0.0658 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.550 - 0.710 g/cc | 0.0199 - 0.0257 lb/in³ | IS 867-1963 |
| Water Absorption | 0.10 - 0.20 % | 0.10 - 0.20 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 55.0 - 70.0 MPa | 7980 - 10200 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 70.0 - 90.0 MPa | 10200 - 13100 psi | 2mm/min.; IS 867-1963 |
| Izod Impact, Notched | 0.500 - 0.650 J/cm | 0.937 - 1.22 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.16228e+11 - 1.00e+12 ohm-cm | 3.16228e+11 - 1.00e+12 ohm-cm | IS 3396-1979 |
| Surface Resistance | 1.00e+11 - 3.16e+11 ohm | 1.00e+11 - 3.16e+11 ohm | IS 3396-1979 |
| Dielectric Strength | 8.50 - 10.0 kV/mm @Temperature 90.0 °C | 216 - 254 kV/in @Temperature 194 °F | IS 2584-1963 |
| Comparative Tracking Index | >= 150 V | >= 150 V | 2824-1975 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 0.917 - 1.33 min | 0.0153 - 0.0222 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |