Momentive Performance Materials PF 2560 Phenolic Formaldehyde Resin, High Surface Quality, For Elect

Momentive Performance Materials PF 2560 Phenolic Formaldehyde Resin, High Surface Quality, For Elect 物性表: Momentive Performance Materials PF 2560 Phenolic Formaldehyde Resin, High Surface Quality, For Elect物性表及特性介绍,Momentive Performance Materials PF 2560 Phenolic Formaldehyde Resin, High Surface Quality, For Elect注塑参数详情,如需Momentive Performance Materials PF 2560 Phenolic Formaldehyde Resin, High Surface Quality, For Elect下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.59
  • 弯曲模量 [MPa]: 9.00
 
Physical PropertiesMetricEnglishComments
Density 1.59 g/cc0.0574 lb/in³ISO 1183
Apparent Bulk Density 0.740 g/cc0.0267 lb/in³ISO 60
Linear Mold Shrinkage, Flow 0.0070 cm/cm0.0070 in/inInjection molding; ISO 2577
 
Mechanical PropertiesMetricEnglishComments
Ball Indentation Hardness 350 MPa50800 psiH 961/30; ISO 2039/P1
Tensile Strength at Break 50.0 MPa7250 psi5 mm/min; ISO 527 - 1/2
Tensile Modulus 9.00 GPa1310 ksi1 mm/min; ISO 527 - 1/2
Flexural Strength 90.0 MPa13100 psi2 mm/min; ISO 178
Flexural Modulus 9.00 GPa1310 ksiISO 178
Compressive Strength 225 MPa32600 psiTest specimen flat tested; ISO 604
Charpy Impact Unnotched 0.550 J/cm²
@Temperature 23.0 °C
2.62 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1/2 eU
Charpy Impact, Notched 0.140 J/cm²
@Temperature 23.0 °C
0.666 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1/2 eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+12 ohm-cm1.00e+12 ohm-cmIEC 60093
Surface Resistance 1.00e+11 ohm1.00e+11 ohmIEC 60093
Dielectric Constant 11
@Frequency 100 Hz
11
@Frequency 100 Hz
IEC 60250
Dielectric Strength 5.00 kV/mm
@Thickness 1.00 mm
127 kV/in
@Thickness 0.0394 in
IEC 60243-P1
Dissipation Factor 0.20
@Frequency 100 Hz
0.20
@Frequency 100 Hz
IEC 60250
Arc Resistance 125 - 130 sec125 - 130 secASTM D495
Comparative Tracking Index 125 V125 VTest liquid A; IEC 60112
 
Thermal PropertiesMetricEnglishComments
Maximum Service Temperature, Air 150 °C302 °F<20000 hours; IEC 60216-P1
 230 °C446 °F< 50 hours; IEC 60216-P1
Deflection Temperature at 8.0 MPa 120 °C248 °FISO 75-2
UL RTI, Electrical 150 °C
@Thickness 1.50 mm
302 °F
@Thickness 0.0591 in
(ALL)
UL RTI, Mechanical with Impact 150 °C
@Thickness 1.50 mm
302 °F
@Thickness 0.0591 in
(ALL)
UL RTI, Mechanical without Impact 150 °C
@Thickness 1.50 mm
302 °F
@Thickness 0.0591 in
(ALL)
Flammability, UL94  V-1
@Thickness 1.50 mm
V-1
@Thickness 0.0591 in
(ALL)
 V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
(BK, NC)
 V-0
@Thickness 3.00 mm
V-0
@Thickness 0.118 in
ALL
Shrinkage 0.40 %0.40 %Injection molding, 168 hours/110°C; ISO 2577
 
Processing PropertiesMetricEnglishComments
Feed Temperature 60.0 - 75.0 °C140 - 167 °FInjection molding
Nozzle Temperature 80.0 - 100 °C176 - 212 °FInjection molding
Melt Temperature 80.0 - 100 °C176 - 212 °FInjection molding
Mold Temperature 160 - 190 °C320 - 374 °FInjection molding
 160 - 190 °C320 - 374 °FCompression molding
Injection Pressure >= 15.0 MPa>= 2180 psiCompression and injection cavity mold pressure
Back Pressure 0.500 - 2.00 MPa72.5 - 290 psiInjection molding
Cure Time 0.167 - 0.333 min0.00278 - 0.00556 hourPer 1 mm of wall thickness, injection molding
 0.333 - 0.667 min0.00556 - 0.0111 hourPer 1 mm of wall thickness, compression molding
 
Descriptive Properties
Chromatic SpectrumAll Colors
Creep Rupture StrengthVery Good
Holding PressureApproximately 40-60% of injection pressure
Media ResistanceVery Good
Moisture Absorption20 mgISO 62, 24 hours at 23°C
Reserves by Peak TemperatureVery High
Thermal ExpansionVery Slight

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-34873.html

免责声明: 本文 Momentive Performance Materials PF 2560 Phenolic Formaldehyde Resin, High Surface Quality, For Elect 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4