- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc @Thickness >=0.000 mm | 0.0470 lb/in³ @Thickness >=0.000 in | 24hr/23°C/50% RH; ISO 1183-A; IEC/EN 61212-2 7.3 |
| Water Absorption | 0.20 % | 0.20 % | 24hr/50°C+24hr in water at 23°C; ISO 62-1; IEC/EN 61212-2 7.2 |
| Mechanical Properties | Metric | English | Comments |
| Flexural Strength | 100 MPa @Diameter >=100 mm | 14500 psi @Diameter >=3.94 in | 24hr/23°C/50% RH; ISO 178; IEC/EN 61212-2 5.1 |
| Compressive Strength | 170 MPa @Temperature 23.0 °C, Time 86400 sec | 24700 psi @Temperature 73.4 °F, Time 24.0 hour | 50% RH, Axial; ISO 604; IEC/EN 61212-2 5.2 |
| Adhesive Bond Strength | 130 MPa @Diameter <=100 mm | 18900 psi @Diameter <=3.94 in | 24hr/23°C/50% RH; IEC 60212-2; IEC/EN 61212-2 5.3 |
| Electrical Properties | Metric | English | Comments |
| Insulation Resistance | 2.00e+8 ohm @Diameter 8.00 - 10.0 mm | 2.00e+8 ohm @Diameter 0.315 - 0.394 in | 24hr/50°C+24h in water at 23°C; IEC; IEC/EN 61212-2 6.2 |
| Dielectric Strength | 3.00 kV/mm @Thickness 3.00 mm | 76.2 kV/in @Thickness 0.118 in | 24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60243-1; IEC/EN 61212-2 6.1.2.1 |
| 0.800 kV/mm @Diameter >=3.00 mm | 20.3 kV/in @Diameter >=0.118 in | 24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60243-1; IEC/EN 61212-2 6.1.2.1 | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Inert | 100 °C @Thickness 3.00 mm, Time 7.20e+7 sec | 212 °F @Thickness 0.118 in, Time 20000 hour | IEC 60695-11-10; IEC/EN 61212-2 7.1 |