- 密度 [g/cm3]: 1.57
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.27
- 断裂伸长率 [%]: 88.0
- 弯曲强度 [MPa]: 41.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Compression; ASTM D955 |
| 0.0065 cm/cm | 0.0065 in/in | Transfer; ASTM D955 | |
| 0.0085 cm/cm | 0.0085 in/in | Injection; ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D651 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Compressive Yield Strength | 193 MPa | 28000 psi | ASTM D695 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.320 J/cm² | 1.52 ft-lb/in² | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Insulation Resistance | 1.00e+9 ohm | 1.00e+9 ohm | After Boiling; ASTM D257 |
| 1.00e+11 ohm | 1.00e+11 ohm | Normal; ASTM D257 | |
| Dielectric Strength | 13.8 kV/mm | 351 kV/in | ASTM D149 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL PLC 4 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Two Hour Heat Resistance per ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.600 mm | V-0 @Thickness 0.0236 in | |