- 密度 [g/cm3]: 0.112
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.112 g/cc | 0.00405 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 5.52 MPa | >= 800 psi | Bare, min |
| >= 7.17 MPa | >= 1040 psi | Stabilized, min | |
| 7.93 MPa | 1150 psi | Bare, typ | |
| 8.96 MPa | 1300 psi | Stabilized, typ | |
| Compressive Modulus | 0.938 GPa | 136 ksi | Stabilized, typ |
| Shear Modulus | 0.0965 GPa | 14.0 ksi | Plate Shear, W Direction, typ |
| 0.207 GPa | 30.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 2.00 MPa | >= 290 psi | Plate Shear, W Direction, min |
| 2.55 MPa | 370 psi | Plate Shear, W Direction, typ | |
| >= 3.52 MPa | >= 510 psi | Plate Shear, L Direction, min | |
| 4.48 MPa | 650 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |