- 密度 [g/cm3]: 0.192
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.192 g/cc | 0.00694 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 12.4 MPa | >= 1800 psi | Bare, min |
| >= 13.5 MPa | >= 1960 psi | Stabilized, min | |
| 15.9 MPa | 2300 psi | Bare, typ | |
| 17.4 MPa | 2520 psi | Stabilized, typ | |
| Compressive Modulus | 1.79 GPa | 260 ksi | Stabilized, typ |
| Shear Modulus | 0.193 GPa | 28.0 ksi | Plate Shear, W Direction, typ |
| 0.303 GPa | 44.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 3.62 MPa | >= 525 psi | Plate Shear, W Direction, min |
| 4.65 MPa | 675 psi | Plate Shear, W Direction, typ | |
| >= 5.62 MPa | >= 815 psi | Plate Shear, L Direction, min | |
| 6.79 MPa | 985 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |