- 拉伸强度 [MPa]: 79.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 - 1.40 g/cc @Thickness 1.57 mm | 1.30 - 1.40 g/cc @Thickness 0.0620 in | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 2.0 % @Thickness 1.57 mm | 2.0 % @Thickness 0.0620 in | ASTM D229 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 85 - 105 @Thickness 1.57 mm | 85 - 105 @Thickness 0.0620 in | ASTM D785 | ||
| Tensile Strength, Yield | 79.3 MPa @Thickness 1.57 mm | 11500 psi @Thickness 0.0620 in | CW; ASTM D638 | ||
| 93.1 MPa @Thickness 1.57 mm | 13500 psi @Thickness 0.0620 in | LW; ASTM D638 | |||
| Flexural Strength | 117 MPa @Thickness 1.57 mm | 17000 psi @Thickness 0.0620 in | CW; ASTM D790 | ||
| 152 MPa @Thickness 1.57 mm | 22000 psi @Thickness 0.0620 in | LW; ASTM D790 | |||
| Compressive Strength | 172 MPa @Thickness 12.7 mm | 25000 psi @Thickness 0.500 in | ASTM D695 | ||
| Shear Strength | 79.3 MPa @Thickness 15.7 mm | 11500 psi @Thickness 0.620 in | ASTM D732 | ||
| Izod Impact, Unnotched | 0.214 J/cm @Thickness 12.7 mm | 0.400 ft-lb/in @Thickness 0.500 in | CW, Cond E-48/50; ASTM D256 | ||
| 0.267 J/cm @Thickness 12.7 mm | 0.500 ft-lb/in @Thickness 0.500 in | LW, Cond E-48/50; ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 6.2 @Thickness 1.57 mm | 6.2 @Thickness 0.0620 in | Permittivity, Cond D-24/23; ASTM D150 | ||
| Dielectric Breakdown | 5000 V @Thickness 1.57 mm | 5000 V @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S/S | ||
| 40000 V @Thickness 1.57 mm | 40000 V @Thickness 0.0620 in | Cond A; ASTM D229 S/S | |||
| Dissipation Factor | 0.052 @Thickness 1.57 mm | 0.052 @Thickness 0.0620 in | Cond D-24/23; ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | HB @Thickness 1.57 mm | HB @Thickness 0.0620 in | |||
| Descriptive Properties | |||||
| Bond Strength | 900 lb | 0.5", ASTM D229 | |||
| Color | Natural, Black | ||||