- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.5
- 缺口冲击强度: 0.24
- 断裂伸长率 [%]: 74.0
- 弯曲强度 [MPa]: 41.0
- 弯曲模量 [MPa]: 6.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.480 g/cc | 0.0173 lb/in³ | ASTM D1895 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Flexural Yield Strength | 74.0 MPa | 10700 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Compressive Yield Strength | 228 MPa | 33100 psi | ASTM D695 |
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 6.00e+9 ohm-cm | 6.00e+9 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.5 @Frequency 1e+6 Hz | 4.5 @Frequency 1e+6 Hz | ASTM D150 |
| 6.0 @Frequency 60 Hz | 6.0 @Frequency 60 Hz | ASTM D150 | |
| Dielectric Strength | 11.8 kV/mm | 300 kV/in | ASTM D149 |
| Dissipation Factor | 0.040 @Frequency 1e+6 Hz | 0.040 @Frequency 1e+6 Hz | ASTM D150 |
| 0.11 @Frequency 60 Hz | 0.11 @Frequency 60 Hz | ASTM D150 | |
| Comparative Tracking Index | 125 V | 125 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 171 °C | 340 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| Flammability, UL94 | V-0 @Thickness 3.18 mm | V-0 @Thickness 0.125 in | |
| V-0 @Thickness 3.18 mm | V-0 @Thickness 0.125 in | ||