- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.3
- 断裂伸长率 [%]: 69.0
- 弯曲强度 [MPa]: 41.0
- 弯曲模量 [MPa]: 10.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ASTM D1895 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Flexural Yield Strength | 69.0 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 10.4 GPa | 1510 ksi | ASTM D790 |
| Compressive Yield Strength | 206 MPa | 29900 psi | ASTM D695 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 6.0 @Frequency 1e+6 Hz | 6.0 @Frequency 1e+6 Hz | ASTM D150 |
| 14 @Frequency 60 Hz | 14 @Frequency 60 Hz | ASTM D150 | |
| Dielectric Strength | 11.8 kV/mm | 300 kV/in | ASTM D149 |
| Dissipation Factor | 0.060 @Frequency 1e+6 Hz | 0.060 @Frequency 1e+6 Hz | ASTM D150 |
| 0.17 @Frequency 60 Hz | 0.17 @Frequency 60 Hz | ASTM D150 | |
| Comparative Tracking Index | 230 V | 230 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| Flammability, UL94 | V-0 @Thickness 1.57 mm | V-0 @Thickness 0.0618 in | |
| V-0 @Thickness 1.57 mm | V-0 @Thickness 0.0618 in | ||