- 拉伸强度 [MPa]: 145.0
- 弯曲模量 [MPa]: 19.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | 8HS form; ASTM D792 | ||
| Volatiles | 2.0 - 5.0 % @Temperature 163 °C | 2.0 - 5.0 % @Temperature 325 °F | 5 min | ||
| Thickness | 381 microns | 15.0 mil | per ply, 8HS form | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 75 | 75 | 8HS form; ASTM D2583 | ||
| Tensile Strength, Yield | 145 MPa @Temperature 23.9 °C | 21000 psi @Temperature 75.0 °F | 0° Direction, Dry; 8HS form; ASTM D638 | ||
| Tensile Modulus | 17.2 GPa @Temperature 23.9 °C | 2500 ksi @Temperature 75.0 °F | 0° Direction, Dry; 8HS form; ASTM D638 | ||
| Flexural Strength | 269 MPa @Temperature 23.9 °C | 39000 psi @Temperature 75.0 °F | Dry; 8HS form; ASTM D790 | ||
| Flexural Modulus | 19.3 GPa @Temperature 23.9 °C | 2800 ksi @Temperature 75.0 °F | Dry; 8HS form; ASTM D790 | ||
| Compressive Strength | 379 MPa @Temperature 23.9 °C | 55000 psi @Temperature 75.0 °F | Dry; 8HS form; ASTM D695 | ||
| Compressive Modulus | 19.3 GPa @Temperature 23.9 °C | 2800 ksi @Temperature 75.0 °F | Dry; 8HS form; ASTM D695 | ||
| Shear Strength | 35.2 MPa @Temperature 23.9 °C | 5100 psi @Temperature 75.0 °F | Short Beam; Dry; 8HS form; ASTM D5379 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 7.20 µm/m-°C @Temperature 204 °C | 4.00 µin/in-°F @Temperature 400 °F | with ply; 8HS form; ASTM D696 | ||
| 12.2 µm/m-°C @Temperature 204 °C | 6.80 µin/in-°F @Temperature 400 °F | x-ply; 8HS form; ASTM D696 | |||
| Specific Heat Capacity | 2.09 J/g-°C | 0.500 BTU/lb-°F | 8HS form; ASTM C351 | ||
| Thermal Conductivity | 0.0720 W/m-K @Temperature 149 °C | 0.500 BTU-in/hr-ft²-°F @Temperature 300 °F | x-ply; 8HS form; ASTM C177 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Fabric Area Weight (g/m²) | 280 | ||||
| Filler Content (%) | 9-15 | ||||
| Prepreg Resin Content (%) | 31-37 | ||||
| Resin Flow (%) | 5-20 | 325°F, 150psi | |||