- 拉伸强度 [MPa]: 331.0
- 弯曲模量 [MPa]: 18.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 g/cc | 1.75 g/cc | ASTM D792 | ||
| Volatiles | 2.0 - 5.0 % @Temperature 135 °C | 2.0 - 5.0 % @Temperature 275 °F | 8 min | ||
| Thickness | 229 microns | 9.00 mil | cured laminate, per ply | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 70 | 70 | ASTM D2583 | ||
| Tensile Strength, Yield | 331 MPa @Temperature 260 °C | 48000 psi @Temperature 500 °F | 0° Direction, Dry; 325°F Autoclave Cured; ASTM D638 | ||
| 352 MPa @Temperature 23.9 °C | 51000 psi @Temperature 75.0 °F | 0° Direction, Dry; 325°F Autoclave Cured; ASTM D638 | |||
| Tensile Modulus | 20.0 GPa @Temperature 260 °C | 2900 ksi @Temperature 500 °F | 0° Direction, Dry; 325°F Autoclave Cured; ASTM D638 | ||
| 25.5 GPa @Temperature 23.9 °C | 3700 ksi @Temperature 75.0 °F | 0° Direction, Dry; 325°F Autoclave Cured; ASTM D638 | |||
| Flexural Strength | 276 MPa @Temperature 260 °C | 40000 psi @Temperature 500 °F | Dry; 325°F Autoclave Cured; ASTM D790 | ||
| 490 MPa @Temperature 23.9 °C | 71000 psi @Temperature 75.0 °F | Dry; 325°F Autoclave Cured; ASTM D790 | |||
| Flexural Modulus | 18.6 GPa @Temperature 260 °C | 2700 ksi @Temperature 500 °F | Dry; 325°F Autoclave Cured; ASTM D790 | ||
| 24.8 GPa @Temperature 23.9 °C | 3600 ksi @Temperature 75.0 °F | Dry; 325°F Autoclave Cured; ASTM D790 | |||
| Compressive Strength | 262 MPa @Temperature 260 °C | 38000 psi @Temperature 500 °F | Dry; 325°F Autoclave Cured; ASTM D695 | ||
| 462 MPa @Temperature 23.9 °C | 67000 psi @Temperature 75.0 °F | Dry; 325°F Autoclave Cured; ASTM D695 | |||
| Compressive Modulus | 20.7 GPa @Temperature 260 °C | 3000 ksi @Temperature 500 °F | Dry; 325°F Autoclave Cured; ASTM D695 | ||
| 24.1 GPa @Temperature 23.9 °C | 3500 ksi @Temperature 75.0 °F | Dry; 325°F Autoclave Cured; ASTM D695 | |||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.17 J/g-°C @Temperature 65.6 °C | 0.280 BTU/lb-°F @Temperature 150 °F | ASTM C351 | ||
| Processing Properties | Metric | English | Comments | ||
| Gel Time | 0.800 - 1.70 min | 0.800 - 1.70 min | |||
| Shelf Life | 3.00 Month @Temperature 4.44 °C | 3.00 Month @Temperature 40.0 °F | |||
| 6.00 Month @Temperature -17.8 °C | 6.00 Month @Temperature 0.000 °F | ||||
| Descriptive Properties | |||||
| Fabric Area Weight (g/m²) | 303 | ||||
| Prepreg Resin Content (%) | 31-37 | ||||
| Resin Flow (%) | 5-20 | 325°F, 15psi | |||