- 密度 [g/cm3]: 1.72
- 缺口冲击强度: 0.32
- 断裂伸长率 [%]: 67.8
- 弯曲强度 [MPa]: 38.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 64 | 64 | |
| Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | |
| Elongation at Break | 0.66 % | 0.66 % | |
| Tensile Modulus | 9.45 GPa | 1370 ksi | |
| Flexural Yield Strength | 67.8 MPa | 9830 psi | |
| Compressive Yield Strength | 133 MPa | 19300 psi | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 15.0 µm/m-°C @Temperature 20.0 °C | 8.33 µin/in-°F @Temperature 68.0 °F | |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.282 W/m-K | 1.96 BTU-in/hr-ft²-°F | |