- 密度 [g/cm3]: 1.89
- 缺口冲击强度: 1.156
- 弯曲强度 [MPa]: 79.0
- 弯曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.89 g/cc | 0.0683 lb/in³ | ASTM D792A |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 94 | 94 | ASTM D785 |
| Hardness, Rockwell M | 109 | 109 | ASTM D785 |
| Tensile Strength, Ultimate | 79.0 MPa | 11500 psi | ASTM D651 |
| Flexural Strength | 114 MPa | 16500 psi | ASTM D790 |
| Flexural Modulus | 17.0 GPa | 2470 ksi | ASTM D790 |
| Compressive Strength | 204 MPa | 29600 psi | ASTM D695 |
| Izod Impact, Notched | 1.156 J/cm | 2.166 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 12.7 kV/mm | 323 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 315 °C | >= 599 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |