- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 0.77
- 缺口冲击强度: 0.945
- 弯曲强度 [MPa]: 44.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792A |
| Water Absorption | 0.77 % | 0.77 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 44.0 MPa | 6380 psi | ASTM D651 |
| Flexural Strength | 128 MPa | 18600 psi | ASTM D790 |
| Compressive Strength | 152 MPa | 22000 psi | ASTM D695 |
| Izod Impact, Notched | 0.945 J/cm | 1.77 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 10.4 kV/mm | 264 kV/in | Short Time; Dry; ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 150 - 175 °C | 302 - 347 °F | |