- 密度 [g/cm3]: 1.7
- 弯曲模量 [MPa]: 12.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | Powder Density; ISO 60 | ||
| Density | 1.70 g/cc | 0.0614 lb/in³ | Relative Density; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | Injection Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 | ||
| Elongation at Break | 0.70 % | 0.70 % | Tensile; ISO 527 | ||
| 1.5 % | 1.5 % | Flexure; ISO 178 | |||
| Tensile Modulus | 15.0 GPa | 2180 ksi | ISO 527 | ||
| Flexural Strength | 160 MPa | 23200 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 | ||
| Compressive Strength | 245 MPa | 35500 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243 | ||
| Comparative Tracking Index | 125 V | 125 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 20.0 °C | 13.9 µin/in-°F @Temperature 68.0 °F | TMA | ||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 20.0 °C | 25.0 µin/in-°F @Temperature 68.0 °F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 Af | ||
| Shrinkage | 0.15 % | 0.15 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| ISO type | PF 2 C1 | ||||
| Main Filler | Glass Fiber & Molybdenum Disulfide | ||||
| Molding Method | Compression, transfer, injection | ||||