- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.08
- 弯曲模量 [MPa]: 12.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.640 g/cc | 0.0231 lb/in³ | ISO 60 | ||
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.080 % | 0.080 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1 | ||
| Elongation at Break | 0.80 % | 0.80 % | ISO 527-1 | ||
| Tensile Modulus | 13.0 GPa | 1890 ksi | ISO 527-1 | ||
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 | ||
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 | ||
| Compressive Strength | 260 MPa | 37700 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.25 J/cm² | 5.95 ft-lb/in² | ISO 179-1 | ||
| Charpy Impact, Notched | 0.380 J/cm² | 1.81 ft-lb/in² | ISO 179-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 7.02e+14 ohm-cm | 7.02e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.91e+13 ohm | 1.91e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | IEC 60243-1 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C | 10.6 µin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C | 30.6 µin/in-°F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 213 °C | >= 415 °F | ISO 75 Af | ||
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||||
| Shrinkage | 0.090 % | 0.090 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Green | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||