- 密度 [g/cm3]: 2.08
- 吸水率 [%]: 0.05
- 弯曲模量 [MPa]: 24.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 60 | ||
| Density | 2.08 g/cc | 0.0751 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.050 % | 0.050 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0016 cm/cm | 0.0016 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527-1 | ||
| Elongation at Break | 0.40 % | 0.40 % | ISO 527-1 | ||
| Tensile Modulus | 28.0 GPa | 4060 ksi | ISO 527-1 | ||
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 | ||
| Flexural Modulus | 24.0 GPa | 3480 ksi | ISO 178 | ||
| Compressive Strength | 360 MPa | 52200 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179-1 | ||
| Charpy Impact, Notched | 0.270 J/cm² | 1.28 ft-lb/in² | ISO 179-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C | 7.78 µin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 211 °C | >= 412 °F | ISO 75 Af | ||
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||||
| Shrinkage | 0.050 % | 0.050 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Dark Green | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||