- 密度 [g/cm3]: 1.63
- 吸水率 [%]: 0.06
- 弯曲模量 [MPa]: 15.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 60 | ||
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.060 % | 0.060 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0044 cm/cm | 0.0044 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-1 | ||
| Elongation at Break | 0.47 % | 0.47 % | ISO 527-1 | ||
| Tensile Modulus | 19.0 GPa | 2760 ksi | ISO 527-1 | ||
| Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 | ||
| Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 | ||
| Compressive Strength | 162 MPa | 23500 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.290 J/cm² | 1.38 ft-lb/in² | ISO 179-1 | ||
| Charpy Impact, Notched | 0.130 J/cm² | 0.619 ft-lb/in² | ISO 179-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 28.0 µm/m-°C | 15.6 µin/in-°F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 166 °C | >= 331 °F | ISO 75 Af | ||
| Shrinkage | 0.080 % | 0.080 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||