- 密度 [g/cm3]: 1.8
- 吸水率 [%]: 0.11
- 弯曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.790 g/cc | 0.0285 lb/in³ | ISO 60 | ||
| Density | 1.80 g/cc | 0.0650 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.11 % | 0.11 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0023 cm/cm | 0.0023 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 114 MPa | 16500 psi | ISO 527-1 | ||
| Elongation at Break | 0.88 % | 0.88 % | ISO 527-1 | ||
| Tensile Modulus | 18.0 GPa | 2610 ksi | ISO 527-1 | ||
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 | ||
| Flexural Modulus | 16.0 GPa | 2320 ksi | ISO 178 | ||
| Compressive Strength | 257 MPa | 37300 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.34 J/cm² | 6.38 ft-lb/in² | ISO 179-1 | ||
| Charpy Impact, Notched | 0.340 J/cm² | 1.62 ft-lb/in² | ISO 179-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.82e+15 ohm-cm | 3.82e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 7.36e+13 ohm | 7.36e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243-1 | ||
| Comparative Tracking Index | 200 V | 200 V | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C | 2.78 µin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | TMA | ||
| Thermal Conductivity | 0.410 W/m-K | 2.85 BTU-in/hr-ft²-°F | ASTM E1461 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 155 °C | >= 311 °F | ISO 75 Af | ||
| Deflection Temperature at 8.0 MPa | 136 °C | 277 °F | ISO 75 Cf | ||
| Shrinkage | 0.070 % | 0.070 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||