- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.4
- 断裂伸长率 [%]: 76.0
- 弯曲强度 [MPa]: 52.0
- 弯曲模量 [MPa]: 8.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.500 g/cc | 0.0181 lb/in³ | ASTM D1895 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 8.30 GPa | 1200 ksi | ASTM D790 |
| Compressive Yield Strength | 207 MPa | 30000 psi | ASTM D695 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.8 | 4.8 | 1MHz; ASTM D150 |
| 7.2 | 7.2 | 60 Hz; ASTM D150 | |
| Dielectric Strength | 13.4 kV/mm | 340 kV/in | ASTM D149 |
| Dissipation Factor | 0.040 | 0.040 | 1 MHz; ASTM D150 |
| 0.14 | 0.14 | 60 Hz; ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 331 °F | ASTM D648 |