- 密度 [g/cm3]: 0.95
- 弯曲强度 [MPa]: 28.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | Uncompounded |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 30 - 100 | 30 - 100 | Depends on compounding |
| Hardness, Shore D | 30 - 45 | 30 - 45 | Depends on compounding |
| Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | Compounded Tire |
| Elongation at Break | 100 - 800 % | 100 - 800 % | |
| 100% Modulus | 0.00150 GPa | 0.218 ksi | |
| Shear Modulus | 0.000500 GPa | 0.0725 ksi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 2.9 @Frequency 1000 Hz | 2.9 @Frequency 1000 Hz | |
| Dielectric Strength | 50.0 kV/mm | 1270 kV/in | Step by step |
| Dissipation Factor | 0.0020 @Frequency 60.0 - 1000 Hz | 0.0020 @Frequency 60.0 - 1000 Hz | |
| 0.030 @Frequency 1e+6 Hz | 0.030 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 225 µm/m-°C @Temperature 20.0 °C | 125 µin/in-°F @Temperature 68.0 °F | |
| Specific Heat Capacity | 0.440 J/g-°C | 0.105 BTU/lb-°F | |
| Thermal Conductivity | 0.150 W/m-K | 1.04 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.526 | 1.526 | |