- 弯曲强度 [MPa]: 2.52
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | Arlon SQA-TMS-024 | ||
| Thickness | 203 microns | 8.00 mil | Arlon SQA-TMS-003 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 87 | 87 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 2.52 MPa | 365 psi | ASTM D412 | ||
| Elongation at Break | 28 % | 28 % | ASTM D412 | ||
| Modulus of Elasticity | 0.0621 GPa | 9.00 ksi | Arlon SQA-TMS-008 | ||
| Poissons Ratio | 0.50 | 0.50 | |||
| Shear Modulus | 0.00183 GPa | 0.265 ksi | ASTM D1002 | ||
| Shear Strength | 0.965 MPa | 140 psi | ASTM D1002 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.602 | 4.602 | IPC TM 650-2.5.5.3 | ||
| Dielectric Strength | 35.4 kV/mm | 900 kV/in | ASTM D149 | ||
| Dissipation Factor | 0.0041 | 0.0041 | IPC TM 650-2.5.5.3 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 52.0 µm/m-°C @Temperature 20.0 °C | 28.9 µin/in-°F @Temperature 68.0 °F | ASTM E 831 | ||
| Specific Heat Capacity | 0.850 J/g-°C @Temperature 100 °C | 0.203 BTU/lb-°F @Temperature 212 °F | Arlon SQA-TMS-052 | ||
| Thermal Conductivity | 3.00 W/m-K | 20.8 BTU-in/hr-ft²-°F | Silicone property; ASTM E1530 | ||
| 3.3867 W/m-K @Temperature 100 °C | 23.504 BTU-in/hr-ft²-°F @Temperature 212 °F | SQA-TMS-054 | |||
| Maximum Service Temperature, Air | 95.6 °C | 204 °F | |||
| Minimum Service Temperature, Air | -73.3 °C | -100 °F | |||
| Glass Transition Temp, Tg | -119 °C | -182 °F | ASTM D3418 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 121 °C | 0.250 hour @Temperature 250 °F | |||
| Shelf Life | 6.00 Month @Temperature 7.00 °C | 6.00 Month @Temperature 44.6 °F | |||
| Descriptive Properties | |||||
| Color | Gray | ||||
| Plasticity (mm) Arlon SQA-TMS-005 | 7.1 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.