- 密度 [g/cm3]: 1.497
- 拉伸强度 [MPa]: 12.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.497 g/cc | 0.05408 lb/in³ | ASTM D3165 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 63 | 63 | ASTM D2240 | ||
| 68.04 @Treatment Temp. 100 °C, Time 252000 sec | 68.04 @Treatment Temp. 212 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Tensile Strength, Yield | 12.1 MPa | 1750 psi | ASTM D412 | ||
| 11.74 MPa @Treatment Temp. 100 °C, Time 252000 sec | 1703 psi @Treatment Temp. 212 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Elongation at Break | 540.8 % | 540.8 % | ASTM D412 | ||
| 430.48 % @Treatment Temp. 100 °C, Time 252000 sec | 430.48 % @Treatment Temp. 212 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Compressive Modulus | 0.000540 GPa @Strain 5.00 % | 0.0783 ksi @Strain 5.00 % | |||
| 0.000790 GPa @Strain 10.0 % | 0.115 ksi @Strain 10.0 % | ||||
| 0.00153 GPa @Strain 20.0 % | 0.222 ksi @Strain 20.0 % | ||||
| 0.00196 GPa @Strain 25.0 % | 0.284 ksi @Strain 25.0 % | ||||
| Compression Set | 6.49 % @Temperature 100 °C, Time 79200 sec | 6.49 % @Temperature 212 °F, Time 22.0 hour | ASTM D395 | ||
| Descriptive Properties | |||||
| Color | Black | ||||