- 密度 [g/cm3]: 1.166
- 拉伸强度 [MPa]: 8.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.166 g/cc | 0.04212 lb/in³ | ASTM D3165 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 54 | 54 | ASTM D2240 | ||
| 59.022 @Treatment Temp. 200 °C, Time 252000 sec | 59.022 @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 | ||
| 6.304 MPa @Treatment Temp. 200 °C, Time 252000 sec | 914.3 psi @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Elongation at Break | 551.6 % | 551.6 % | ASTM D412 | ||
| 345.85 % @Treatment Temp. 200 °C, Time 252000 sec | 345.85 % @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Compressive Modulus | 0.000390 GPa @Strain 5.00 % | 0.0566 ksi @Strain 5.00 % | |||
| 0.000710 GPa @Strain 10.0 % | 0.103 ksi @Strain 10.0 % | ||||
| 0.00140 GPa @Strain 20.0 % | 0.203 ksi @Strain 20.0 % | ||||
| 0.00174 GPa @Strain 25.0 % | 0.252 ksi @Strain 25.0 % | ||||
| Compression Set | 6.43 % @Temperature 175 °C, Time 79200 sec | 6.43 % @Temperature 347 °F, Time 22.0 hour | ASTM D395 | ||
| Descriptive Properties | |||||
| Color | Orange | ||||