| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Apparent Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | MSZ ISO 60 | ||
| Particle Size | 600 µm | 600 µm | <1% above | ||
| Viscosity | 2.50e+6 cP @Shear Rate 200 1/s, Temperature 190 °C | 2.50e+6 cP @Shear Rate 200 1/s, Temperature 374 °F | Capillary viscosimeter | ||
| Mooney Viscosity | 70 @Temperature 120 °C | 70 @Temperature 248 °F | ML(1+4); MSZ 11093 ISO 289 | ||
| Crystallinity | <= 1.0 % | <= 1.0 % | Residual; DSC BC HSz 325 | ||
| Collected Volatile Condensable Material | <= 0.30 % | <= 0.30 % | ISO 1269 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | MSZ ISO 868 | ||
| Tensile Strength at Break | 14.0 MPa | 2030 psi | MSZ ISO 527 | ||
| Elongation at Break | 600 % | 600 % | MSZ ISO 527 | ||
| 100% Modulus | 0.00120 GPa | 0.174 ksi | MSZ ISO 527 | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 4.50 °C | 40.1 °F | DMA method 1 Hz | ||
| Descriptive Properties | |||||
| Chlorine Content, % | 36 | ||||
| Heat Stability at 180°C, minutes | 8 | ||||