| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.70 - 2.20 g/cc | 1.70 - 2.20 g/cc | ASTM D792 | ||
| 1.75 - 2.25 g/cc | 1.75 - 2.25 g/cc | Base Material; ASTM D792 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 75 | 75 | Base Material; ASTM D2240 | ||
| Tensile Strength at Break | >= 1.24 MPa | >= 180 psi | Base Material; ASTM D412 | ||
| 2.41 MPa | 350 psi | Reinforced Material - Fill; ASTM D412 | |||
| 4.48 MPa | 650 psi | Reinforced Material, warp; ASTM D412 | |||
| Elongation at Break | >= 50 % | >= 50 % | Reinforced Material - Fill/Warp; ASTM D412 | ||
| >= 100 % | >= 100 % | Base Material; ASTM D412 | |||
| Tear Strength | 6.125 kN/m | 34.95 pli | Base Material; ASTM D624 | ||
| 30.625 kN/m | 174.75 pli | Reinforced Material - Warp/Fill; ASTM D624 | |||
| Compression Set | 35 % | 35 % | 70 hrs @ 100°C; ASTM D395 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 0.012 ohm-cm | 0.012 ohm-cm | Reinforced Material; MIL-G-83528 | ||
| 0.012 ohm-cm | 0.012 ohm-cm | Base Material; MIL-G-83528 | |||
| <= 0.015 ohm-cm | <= 0.015 ohm-cm | Post Tensile Strength; MIL-G-83528 | |||
| Shielding Effectiveness | >= 55 dB | >= 55 dB | 200 kHz (H Field) - Base/Reinforced Material; MIL-G-83528 | ||
| >= 90 dB | >= 90 dB | 10 GHz (Plane Wave) - Base/Reinforced Material; MIL-G-83528 | |||
| >= 95 dB | >= 95 dB | 2 GHz (Plane Wave) - Base/Reinforced Material; MIL-G-83528 | |||
| >= 100 dB | >= 100 dB | 500 MHz (E Field) - Base/Reinforced Material; MIL-G-83528 | |||
| >= 110 dB | >= 110 dB | 100 MHz (E Field) - Base/Reinforced Material; MIL-G-83528 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 125 °C | 257 °F | |||
| Descriptive Properties | |||||
| Binder | Fluorosilicone | ||||
| EMP Survivability kA / in, min | 0.9 | ||||
| Filler | Ag/Al, Reinforced Material | ||||
| Grade | Military-Aerospace | ||||
| Heat Aging - Base Material ohm-cm max | 0.015 | ||||
| Heat Aging - Reinforced Material ohm-cm max | 0.015 | ||||
| Low Temp Flex - Base Material, TR10 °C, min | -55 | ||||
| Low Temp Flex - Reinforced Material, TR10 °C, min | -55 | ||||
| Vibration Res, After - Base Material ohm-cm max | 0.012 | ||||
| 0.012 | |||||
| Vibration Res, During - Base Material ohm-cm max | 0.015 | ||||
| 0.015 | |||||