| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 - 2.25 g/cc | 1.75 - 2.25 g/cc | ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 55 - 75 | 55 - 75 | ASTM D2240 | ||
| Tensile Strength at Break | >= 1.38 MPa | >= 200 psi | ASTM D412 | ||
| Tensile Strength | 1.40 MPa | 203 psi | Test 2; ASTM D412 | ||
| 1.19 MPa @Temperature 22.0 °C, Time 252000 sec | 172 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Vinyl Protectant; ASTM D412 | |||
| 1.21 MPa @Temperature 22.0 °C, Time 252000 sec | 175 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Tire Cleaner; ASTM D412 | |||
| 1.23 MPa @Temperature 22.0 °C, Time 252000 sec | 178 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to ClearVue®; ASTM D412 | |||
| 1.36 MPa @Temperature 22.0 °C, Time 252000 sec | 197 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Formula 409®; ASTM D412 | |||
| 1.37 MPa @Temperature 22.0 °C, Time 252000 sec | 199 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Cola; ASTM D412 | |||
| 1.37 MPa @Temperature 22.0 °C, Time 252000 sec | 199 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Tap Water; ASTM D412 | |||
| 1.39 MPa @Temperature 22.0 °C, Time 252000 sec | 202 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Windex®; ASTM D412 | |||
| 1.43 MPa @Temperature 22.0 °C, Time 252000 sec | 207 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Carpet Cleaner; ASTM D412 | |||
| 1.43 MPa @Temperature 22.0 °C, Time 252000 sec | 207 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Hairspray; ASTM D412 | |||
| 1.43 MPa @Temperature 22.0 °C, Time 252000 sec | 207 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Windshield Washer Solvent; ASTM D412 | |||
| 1.45 MPa @Temperature 22.0 °C, Time 252000 sec | 211 psi @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Coffee; ASTM D412 | |||
| Elongation at Break | >= 100 % | >= 100 % | ASTM D412 | ||
| 289 % | 289 % | Test 1; ASTM D412 | |||
| 414 % | 414 % | Test 2; ASTM D412 | |||
| 166 % @Temperature 22.0 °C, Time 252000 sec | 166 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Windex®; ASTM D412 | |||
| 219 % @Temperature 22.0 °C, Time 252000 sec | 219 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Formula 409®; ASTM D412 | |||
| 317 % @Temperature 22.0 °C, Time 252000 sec | 317 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to ClearVue®; ASTM D412 | |||
| 326 % @Temperature 22.0 °C, Time 252000 sec | 326 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Hairspray; ASTM D412 | |||
| 418 % @Temperature 22.0 °C, Time 252000 sec | 418 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Tire Cleaner; ASTM D412 | |||
| 418 % @Temperature 22.0 °C, Time 252000 sec | 418 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Windshield Washer Solvent; ASTM D412 | |||
| 433 % @Temperature 22.0 °C, Time 252000 sec | 433 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Vinyl Protectant; ASTM D412 | |||
| 433 % @Temperature 22.0 °C, Time 252000 sec | 433 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Cola; ASTM D412 | |||
| 439 % @Temperature 22.0 °C, Time 252000 sec | 439 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Coffee; ASTM D412 | |||
| 439 % @Temperature 22.0 °C, Time 252000 sec | 439 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Tap Water; ASTM D412 | |||
| 443 % @Temperature 22.0 °C, Time 252000 sec | 443 % @Temperature 71.6 °F, Time 70.0 hour | 50% RH, Exposure to Carpet Cleaner; ASTM D412 | |||
| Tear Strength | 8.75 kN/m | 49.9 pli | ASTM D624 | ||
| Compression Set | <= 30 % @Temperature 100 °C, Time 252000 sec | <= 30 % @Temperature 212 °F, Time 70.0 hour | ASTM D395 Method B | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 0.10 ohm-cm | 0.10 ohm-cm | as supplied without pressure sensitive adhesive; CEPS-0002 | ||
| Shielding Effectiveness | >= 75 dB @Frequency 4.00e+10 Hz | >= 75 dB @Frequency 4.00e+10 Hz | E Field; CHO-TM-TP08 | ||
| >= 100 dB @Frequency 1.00e+8 Hz | >= 100 dB @Frequency 1.00e+8 Hz | E Field; CHO-TM-TP08 | |||
| >= 100 dB @Frequency 5.00e+8 Hz | >= 100 dB @Frequency 5.00e+8 Hz | Plane Wave; CHO-TM-TP08 | |||
| >= 100 dB @Frequency 2.00e+9 Hz | >= 100 dB @Frequency 2.00e+9 Hz | Plane Wave; CHO-TM-TP08 | |||
| >= 100 dB @Frequency 1.00e+10 Hz | >= 100 dB @Frequency 1.00e+10 Hz | Plane Wave; CHO-TM-TP08 | |||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.800 W/m-K @Pressure 2.07 MPa | 5.55 BTU-in/hr-ft²-°F @Pressure 300 psi | ASTM D5470 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | |||
| Minimum Service Temperature, Air | -45.0 °C | -49.0 °F | Flex TR10; ASTM D1329 | ||
| Flammability, UL94 | HB | HB | |||
| Descriptive Properties | |||||
| Binder | Silicone | ||||
| Filler | Ni/C | ||||
| Heat Aging | <0.25 ohm-cm | 125°C for 48 hrs; CEPS-0002 | |||