- 密度 [g/cm3]: 1.8
- 弯曲强度 [MPa]: 49.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | |
| Viscosity | 22000 cP | 22000 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75 | 75 | |
| Tensile Strength, Ultimate | 49.6 MPa | 7200 psi | |
| Elongation at Break | 0.20 % | 0.20 % | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 5.76 W/m-K | 40.0 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| Shrinkage | 0.80 % | 0.80 % | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min | 0.333 hour | at 250°F |