- 拉伸强度 [MPa]: 3.4
- 脆化温度 [℃]: -25.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | at 25°C |
| Mooney Viscosity | 32 @Temperature 121 °C | 32 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 70 | 70 | Peak value, at 25°C |
| Tensile Strength at Break | 16.4 MPa | 2380 psi | |
| Tensile Strength, Yield | 3.40 MPa @Strain 100 % | 493 psi @Strain 100 % | |
| Elongation at Break | 300 % | 300 % | |
| Tear Strength | 23.5 kN/m | 134 pli | at 25°C |
| Taber Abrasion, mg/1000 Cycles | 250 | 250 | H-22 abrasive wheel, load: 1000g x 2 |
| Compression Set | 20 % | 20 % | 70 hours at 25°C |
| 11 % @Temperature 100 °C | 11 % @Temperature 212 °F | 70 hours | |
| 15 % @Temperature 175 °C | 15 % @Temperature 347 °F | 70 hours | |
| 26 % @Temperature 200 °C | 26 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -18.0 °C | -0.400 °F | TR test, TR10 |
| -15.5 °C | 4.10 °F | Gehman torsion test, T10 | |
| -8.00 °C | 17.6 °F | TR test, TR70 | |
| -8.00 °C | 17.6 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -25.0 °C | -13.0 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 4.00 min | 0.0667 hour | Curelastmeter |