- 拉伸强度 [MPa]: 5.0
- 脆化温度 [℃]: -17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | at 25°C |
| Mooney Viscosity | 30 @Temperature 121 °C | 30 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 72 | 72 | Peak value, at 25°C |
| Tensile Strength at Break | 15.1 MPa | 2190 psi | |
| Tensile Strength, Yield | 5.00 MPa @Strain 100 % | 725 psi @Strain 100 % | |
| Elongation at Break | 190 % | 190 % | |
| Tear Strength | 19.6 kN/m | 112 pli | at 25°C |
| Compression Set | 8.0 % | 8.0 % | 70 hours at 25°C |
| 5.0 % @Temperature 100 °C | 5.0 % @Temperature 212 °F | 70 hours | |
| 11 % @Temperature 175 °C | 11 % @Temperature 347 °F | 70 hours | |
| 18 % @Temperature 200 °C | 18 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -18.0 °C | -0.400 °F | TR test, TR10 |
| -13.0 °C | 8.60 °F | Gehman torsion test, T10 | |
| -9.00 °C | 15.8 °F | TR test, TR70 | |
| -6.00 °C | 21.2 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -17.0 °C | 1.40 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Cure Time | 2.80 min | 0.0467 hour | Curelastmeter |