- 拉伸强度 [MPa]: 2.7
- 脆化温度 [℃]: -26.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.89 g/cc | 1.89 g/cc | at 25°C |
| Mooney Viscosity | 34 @Temperature 121 °C | 34 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 68 | 68 | Peak value, at 25°C |
| Tensile Strength at Break | 12.5 MPa | 1810 psi | |
| Tensile Strength, Yield | 2.70 MPa @Strain 100 % | 392 psi @Strain 100 % | |
| Elongation at Break | 300 % | 300 % | |
| Tear Strength | 20.5 kN/m | 117 pli | at 25°C |
| Compression Set | 26 % | 26 % | 70 hours at 25°C |
| 16 % @Temperature 100 °C | 16 % @Temperature 212 °F | 70 hours | |
| 20 % @Temperature 175 °C | 20 % @Temperature 347 °F | 70 hours | |
| 28 % @Temperature 200 °C | 28 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -14.0 °C | 6.80 °F | TR test, TR10 |
| -13.5 °C | 7.70 °F | Gehman torsion test, T10 | |
| -8.00 °C | 17.6 °F | TR test, TR70 | |
| -4.00 °C | 24.8 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -26.0 °C | -14.8 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 9.50 min | 0.158 hour | Curelastmeter |