- 拉伸强度 [MPa]: 2.0
- 脆化温度 [℃]: -25.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | at 25°C |
| Mooney Viscosity | 37 @Temperature 121 °C | 37 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 66 | 66 | Peak value, at 25°C |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | |
| Tensile Strength, Yield | 2.00 MPa @Strain 100 % | 290 psi @Strain 100 % | |
| Elongation at Break | 450 % | 450 % | |
| Tear Strength | 20.6 kN/m | 118 pli | at 25°C |
| Taber Abrasion, mg/1000 Cycles | 155 | 155 | H-22 abrasive wheel, load: 1000g x 2 |
| Compression Set | 21 % | 21 % | 70 hours at 25°C |
| 17 % @Temperature 100 °C | 17 % @Temperature 212 °F | 70 hours | |
| 25 % @Temperature 175 °C | 25 % @Temperature 347 °F | 70 hours | |
| 38 % @Temperature 200 °C | 38 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -19.0 °C | -2.20 °F | TR test, TR10 |
| -15.5 °C | 4.10 °F | Gehman torsion test, T10 | |
| -10.0 °C | 14.0 °F | TR test, TR70 | |
| -10.0 °C | 14.0 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -25.0 °C | -13.0 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 2.50 min | 0.0417 hour | Curelastmeter |