- 弯曲强度 [MPa]: 16.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Mooney Viscosity | 50 @Temperature 100 °C | 50 @Temperature 212 °F | ML(1+4), mu | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 67 | 67 | Cured 10 minutes at 180°C | ||
| Tensile Strength, Ultimate | 16.9 MPa | 2450 psi | Cured 10 minutes at 180°C | ||
| Elongation at Break | 232 % | 232 % | Cured 10 minutes at 180°C | ||
| 100% Modulus | 0.00670 GPa | 0.972 ksi | Cured 10 minutes at 180°C | ||
| Compression Set | 47.5 % | 47.5 % | 168 hrs at 150°C | ||
| Descriptive Properties | |||||
| Armeen® 18D | 0.5 phr | ||||
| HVA® #2 coagent | 2 phr | ||||
| Mooney Scorch at 135°C, Minimum Viscosity | 12.9 | Mooney units | |||
| Mooney Scorch at 135°C, t10 | 13.8 metric minutes | Time for 10 unit rise | |||
| Mooney Scorch at 135°C, t3 | 9.5 metric minutes | Time for 3 unit rise | |||
| N550 Black | 55 phr | ||||
| Naugard® 445 antioxidant | 1 phr | ||||
| Stearic Acid | 0.5 phr | ||||
| Vamac® DP | 100 phr | ||||
| Vanfre® VAM | 1.25 phr | ||||
| Vulcup® 40LE peroxide | 4.5 phr | ||||