- 弯曲强度 [MPa]: 18.4
- 脆化温度 [℃]: -18.0
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 84 | 84 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D2240-91 |
Tensile Strength, Ultimate | 18.4 MPa | 2670 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
Elongation at Break | 105 % | 105 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
100% Modulus | 0.0178 GPa | 2.58 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
Tear Strength | 28.3 kN/m | 161 pli | Die C, Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
Compression Set | 26 % @Temperature 200 °C | 26 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414-94 |
Thermal Properties | Metric | English | Comments |
Brittleness Temperature | -18.0 °C | -0.400 °F | Temperature Retraction, TR-10, using 50% elongation; ASTM D1329-88 |