- 弯曲强度 [MPa]: 10.2
- 脆化温度 [℃]: -18.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 54 | 54 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tensile Strength, Ultimate | 10.2 MPa | 1480 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Elongation at Break | 250 % | 250 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| 100% Modulus | 0.00230 GPa | 0.334 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Compression Set | 8.0 % @Temperature 200 °C | 8.0 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -18.0 °C | -0.400 °F | Temperature Retraction, TR-10; ASTM D1329 |
| Glass Transition Temp, Tg | -19.0 °C | -2.20 °F | DSC |