- 弯曲强度 [MPa]: 13.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 54 @Temperature 121 °C | 54 @Temperature 250 °F | ML 1 + 10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 78 | 78 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Tensile Strength, Ultimate | 13.2 MPa | 1910 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Elongation at Break | 240 % | 240 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| 100% Modulus | 0.00510 GPa | 0.740 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 34 % @Temperature 200 °C | 34 % @Temperature 392 °F | Method B, Plied Disks, 70 hr |