- 弯曲强度 [MPa]: 17.8
- 脆化温度 [℃]: -31.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 66 @Temperature 121 °C | 66 @Temperature 250 °F | ML-10 (gum)-Akron data |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 67 | 67 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 17.8 MPa | 2580 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 267 % | 267 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000600 GPa | 0.0870 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00360 GPa | 0.522 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 11 % @Temperature 200 °C | 11 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Cured 7 min at 177°C and Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -31.4 °C | -24.5 °F | TR-10 |
| Glass Transition Temp, Tg | -32.9 °C | -27.2 °F | DSC |