- 弯曲强度 [MPa]: 20.7
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 72 | 72 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 269 % | 269 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00540 GPa | 0.783 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 17 % @Temperature 200 °C | 17 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Post Cured 2 hr at 232°C) |