Cytec EN-9 (OZR) (Conap) Casting, Potting, and Molding Compound

Cytec EN-9 (OZR) (Conap) Casting, Potting, and Molding Compound 物性表: Cytec EN-9 (OZR) (Conap) Casting, Potting, and Molding Compound物性表及特性介绍,Cytec EN-9 (OZR) (Conap) Casting, Potting, and Molding Compound注塑参数详情,如需Cytec EN-9 (OZR) (Conap) Casting, Potting, and Molding Compound下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.01
  • 吸水率 [%]: 0.2
  • 弯曲强度 [MPa]: 13.8
 
Physical PropertiesMetricEnglishComments
Density 1.01 g/cc0.0365 lb/in³
Water Absorption 0.20 %0.20 %24 hours
Water Absorption at Saturation 0.0040 %0.0040 %30 Days
Viscosity 6800 cP
@Temperature 25.0 °C
6800 cP
@Temperature 77.0 °F
Linear Mold Shrinkage 0.010 cm/cm0.010 in/in
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore A 9090Tolerance of +/- 5
Tensile Strength, Ultimate 13.8 MPa2000 psi
Elongation at Break 450 %450 %
Tear Strength 48.2 kN/m275 pli
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity <= 3.42e+15 ohm-cm<= 3.42e+15 ohm-cm
Insulation Resistance >= 2.50e+13 ohm>= 2.50e+13 ohmValue at 25°C
Dielectric Constant  2.81
@Frequency 1e+6 Hz
2.81
@Frequency 1e+6 Hz
 3.03
@Frequency 100 Hz
3.03
@Frequency 100 Hz
Dielectric Strength 24.0 kV/mm
@Thickness 1.59 mm,
Temperature 25.0 °C
610 kV/in
@Thickness 0.0625 in,
Temperature 77.0 °F
Dissipation Factor  0.010
@Frequency 1e+6 Hz
0.010
@Frequency 1e+6 Hz
 0.031
@Frequency 100 Hz
0.031
@Frequency 100 Hz
Arc Resistance >= 120 sec>= 120 secValue at 25°C
 
Processing PropertiesMetricEnglishComments
Cure Time 960 min16.0 hour80°C
 10080 - 14400 min168.0 - 240 hour25°C
Pot Life 70 min70 minValue for 0.5 lbm at 25°C
 
Descriptive Properties
ColorOpaque Amber

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-36762.html

免责声明: 本文 Cytec EN-9 (OZR) (Conap) Casting, Potting, and Molding Compound 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4