- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 0.4
- 弯曲强度 [MPa]: 4.14
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |||
| Water Absorption | 0.40 % | 0.40 % | 24 hours | ||
| Viscosity | 1500 cP @Temperature 25.0 °C | 1500 cP @Temperature 77.0 °F | |||
| Linear Mold Shrinkage | 0.0115 cm/cm | 0.0115 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 65 | 65 | Tolerance of +/- 5 | ||
| Tensile Strength, Ultimate | 4.14 MPa | 600 psi | |||
| Elongation at Break | 130 % | 130 % | |||
| Tear Strength | 6.14 kN/m | 35.0 pli | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 6.30e+13 ohm-cm | <= 6.30e+13 ohm-cm | |||
| Insulation Resistance | 3.90e+12 ohm | 3.90e+12 ohm | Value at 25°C | ||
| Dielectric Constant | 3.13 @Frequency 1e+6 Hz | 3.13 @Frequency 1e+6 Hz | |||
| 4.7 @Frequency 100 Hz | 4.7 @Frequency 100 Hz | ||||
| Dielectric Strength | 23.1 kV/mm @Thickness 1.59 mm, Temperature 25.0 °C | 588 kV/in @Thickness 0.0625 in, Temperature 77.0 °F | |||
| Dissipation Factor | 0.011 @Frequency 1e+6 Hz | 0.011 @Frequency 1e+6 Hz | |||
| 0.151 @Frequency 100 Hz | 0.151 @Frequency 100 Hz | ||||
| Arc Resistance | >= 120 sec | >= 120 sec | Value at 25°C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 960 min | 16.0 hour | 80°C | ||
| 10080 - 14400 min | 168.0 - 240 hour | 25°C | |||
| Pot Life | 35 min | 35 min | Value for 0.5 lbm at 25°C | ||
| Descriptive Properties | |||||
| Color | Opaque Amber | ||||