- 密度 [g/cm3]: 1.18
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 88 | 88 | Cured; ASTM D2240 | ||
| Tensile Strength at Break | 16.5 MPa | 2400 psi | ASTM D412 | ||
| Elongation at Break | <= 500 % | <= 500 % | ASTM D412 | ||
| Tear Strength | 48.2 kN/m | 275 pli | ASTM D624 | ||
| Taber Abrasion, mg/1000 Cycles | 220 | 220 | H-18 wheel (1000 gram load) | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 13.8 kV/mm | 350 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 48.9 °C | 120 °F | wet | ||
| 82.2 °C | 180 °F | dry | |||
| Shrinkage | 0.14 % | 0.14 % | Cured; ASTM D2566 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 180 min | 3.00 hour | Functional cure | ||
| Pot Life | 8.0 min | 8.0 min | at 75°F | ||
| Descriptive Properties | |||||
| Coverage per pound, in² @ 1/4" thickness | 94 | ||||
| Mix ratio by weight (Resin:Hardener) | 80:20 | ||||